Abstract
The crack-closure effect is a crucial factor that affects the crack growth rate and should be considered in simulation analysis and testing. A mixed-mode I + II loading fatigue crack growth test was performed using EA4T axle steel specimens. The variation of the plastic-induced crack closure (PICC) effect and the roughness-induced crack closure (RICC) effect during crack deflection in the mixed-mode is examined in this study. The results show that the load perpendicular to the crack propagation direction hinders the slip effect caused by the load parallel to the crack propagation direction under mixed-mode loading, and the crack deflection is an intuitive manifestation of the interaction between the PICC and RICC. The proportion of the RA value change on the crack side caused by contact friction was reduced by the interaction between PICC and RICC. The roughness of the crack surface before and after the crack deflection is different, and the spatial torsion crack surface is formed during the crack propagation process. With the increase of the crack length, the roughness of the fracture surface increases. During the crack deflection process, the PICC value fluctuates around 0.2, and the RICC value is increased to 0.15.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.