Abstract
GaAs(001) surfaces treated with ultrasonic running deionized water (URDIW), after being etched by H 2SO 4 or NH 4OH were examined by using X-ray photoelectron spectroscopy (XPS) and reflection high-energy electron diffraction (RHEED), XPS analysis revealed that the arsenic and gallium oxides on chemically etched surfaces were completely removed by the URDIW treatment. RHEED observation indicated that the H 2SO 4-etched GaAs surface shows a streaky (2×1) surface reconstruction pattern at 360°C and that the NH 4OH-etched surfaces show a (2×4) surface reconstruction pattern at 310°C. These experimental results indicate that chemically clean GaAs surfaces with little damage can be produced by URDIW treatment and that the stoichiometry of a URDIW treated surface can be controlled by varying the etching solutions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.