Abstract
Oxide dispersion strengthened (ODS) steels exhibit exceptional radiation resistance and high-temperature creep strength when compared to traditional ferritic and ferritic/martensitic (F/M) steels. Their excellent mechanical properties result from very fine nanoparticles dispersed within the matrix. In this work, we applied a high-energy synchrotron radiation X-ray to study the deformation process of a 9Cr ODS steel. The load partitioning between the ferrite/martensite and the nanoparticles was observed during sample yielding. During plastic deformation, the nanoparticles experienced a dramatic loading process, and the internal stress on the nanoparticles increased to a maximum value of 3.7 GPa, which was much higher than the maximum applied stress (∼986 MPa). After necking, the loading capacity of the nanoparticles was significantly decreased due to a debonding of the particles from the matrix, as indicated by a decline in lattice strain/internal stress. Due to the load partitioning, the ferrite/martensite slightly relaxed during early yielding, and slowly strained until failure. This study develops a better understanding of loading behavior for various phases in the ODS F/M steel.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.