Abstract
ABSTRACT A novel, two-step, solid-state method to produce complex geometry titanium parts was investigated by combining Cold Isostatic Pressing (CIP) with Field Assisted Sintering Technology (FAST). Hydride-dehydride powders of commercially pure titanium and Ti-6Al-4V were CIP’ed into shaped compacts using silicone moulds, then further consolidated using FAST, with ZrO2 powder as a secondary pressing media. The final parts retained the complex features from the CIP moulds but were compressed in the pressing axis. Densities >99% were achieved, with optimised FAST processing parameters required for the different alloys. High hardness and fine equiaxed microstructures were observed at the edges of the parts, suggesting oxygen transfer from the ZrO2 pressing media had occurred, with more investigation needed to better understand and prevent this. Despite this, the CIP-FAST process route has been demonstrated to be a fast, low-cost and material-efficient option to produce a wide variety of complex titanium parts.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.