Abstract
Bulk doping, surface coating, and size reducing are three strategies for improving the electrochemical properties of Li4Ti5O12 (LTO). In this work, chromium (Cr)-modified LTO with a synergistic effect of bulk doping, surface coating, and size reducing is synthesized by a facile sol-gel method. X-ray diffraction (XRD) and Raman analysis prove that Cr dopes into the LTO bulk lattice, which effectively inhibits the generation of TiO2 impurities. Transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) verifies the surface coating of Li2CrO4 on the LTO surface, which decreases impedance of the LTO electrode. More importantly, the size of LTO particles can be significantly reduced from submicroscale to nanoscale as a result of the protection of the Li2CrO4 surface layer and the suppression from Cr atoms on the long-range order in the LTO lattice. As anode material, Li4-xCr3xTi5-2xO12 (x = 0.1) delivers a reversible capacity of 141 mAh g(-1) at 10 °C, and over 155 mAh g(-1) at 1 °C after 1000 cycles. Therefore, the Cr-modified Li4Ti5O12 prepared via a sol-gel method has potential for applications in high-power, long-life lithium-ion batteries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.