Abstract
The corrosion behavior of steel in cracked ordinary portland cement (OPC) and portland pozzolana cement (PPC) concretes when exposed to a chloride-rich environment is presented here. Three water-to-cement (w/c) ratios, and precrack widths of 0.2 and 0.4 mm were studied. A simple U-shaped specimen with precracks under flexural load was used in the study; the specimen has a deformed steel bar of 12 mm diameter placed at the bottom with 20 mm clear cover. Measurements made include chloride ion penetrability, sorptivity, half-cell potential, resistivity, total charge passed and gravimetric weight loss. The chloride ion penetrability of PPC was found to be nearly three times lower than that of OPC. The reduction in the gravimetric weight loss of rebars in PPC with respect to those in OPC is in the range of about 1.5 to 2.0 in the case of precracked concretes. The reduction in diameter (i.e., caused by pitting) is higher for OPCs. Studies showed that PPC is significantly superior to the corresponding uncracked ...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.