Abstract
Cross-linked chitin/deacetylated chitin nanocomposite films can be considered as a potential industrial adsorbent for the removal of organic pollutants for water purification. Chitin (C) and deacetylated chitin (dC) nanofibers were extracted from raw chitin and characterized using FTIR, XRD and TGA techniques. The TEM image confirmed the formation of chitin nanofibers with a diameter range of 10–45 nm. The deacetylated chitin nanofibers (DDA-46 %) having 30 nm diameter was evidenced using FESEM. Further, the C/dC nanofibers were prepared at different ratios (80/20, 70/30, 60/40 & 50/50 ratios) and cross-linked. The highest tensile strength of 40 MPa and Young's modulus of 3872 MPa was exhibited by 50/50C/dC. The DMA studies revealed that the storage modulus enhanced by 86 % for 50/50C/dC (9.06 GPa) in comparison to 80/20C/dC nanocomposite. Further, the 50/50C/dC exhibited a maximum adsorption capacity of 30.8 mg/g at pH = 4 in 30 mg/L of Methyl Orange (MO) dye within 120 min. The experimental data agreed with pseudo-second-order model indicating chemisorption process. The adsorption isotherm data was best described by Freundlich model. The nanocomposite film is an effective adsorbent that can be regenerated and recycled for five adsorption-desorption cycle.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Biological Macromolecules
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.