Chemiresistive room temperature H2S sensor based on CunO nanoflowers fabricated by laser ablation

Abstract

Hierarchical CunO nanoflowers were synthesized through the laser ablation of a CuO target in NaOH solutions for room-temperature (27 ℃) H2S detection. Notably, the pH value of NaOH solutions influenced both the micro-morphologies and compositions of the CunO products, as evidenced by XRD, XPS, SEM and TEM. In high pH solutions, the specific surface area of the CunO products increased, their thickness decreased, and the Cu2O content diminished, resulting in enhanced sensitivity, selectivity and stability of the CunO products’ response to H2S. Notably, the pH14# sample synthesized using an NaOH solution with a pH value of 14 featured pure CuO nanoflowers comprising slightly curled nanosheets with a thickness of approximately 10 nm. This sensor demonstrated excellent H2S sensing performance at room temperature, exhibiting a response value of 1.17 for 10 ppb H2S, along with high selectivity and good long-term stability. However, after exposure to H2S, the resistance of the sensor did not recover to its baseline in air at room temperature. Thermogravimetry results revealed that a temperature of 300 °C was effective for recovery of the sensor. Consequently, the operation temperature of the pH14# sensor was controlled using a micro-hotplate. In the pulse heating mode, the sensor’s response to 100 ppb H2S was 1.5, with a response time of 135 s and a recovery time of 137 s.