Abstract
The influence of the microstructure on the electrical properties and polarization behavior of thin porous ceramic electrodelayers used in solid oxide fuel cells has been investigated. Thin layers (2–10 µm) of the cathode materialSr0.15La0.85MnO3 (15SLM) were film coated on YSZ substrates from classified suspensions. Narrow particle-size distributionsin the suspension resulted in close-packed layers with a very homogeneous porosity and pore-size distribution. Thespecific conductivity of the layers decreased significantly with increasing porosity and mean pore size. A specific conductivityof 109 S · cm–1 was obtained at 1000°C for a 2.9 µm thick layer from a suspension with particles in the range 0.10–0.25 µm. The current-overvoltage behavior of the film-coated layers presented in this study did not, however, show anysignificant dependence on the thickness and the microstructure of the porous layers. Overvoltages (eta) at a current densityof 0.1 A/cm2 at 898°C were quite low, i.e., in the range 60–70 mV. In comparison with other studies it is shown that filmcoating improves the microstructure of the ceramic electrode layers, which in turn lowers the cathodic overvoltages forthe oxygen reduction reaction.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.