Abstract
This contribution presents the characterization of poly(acrylamide-co-acrylic acid)-grafted-poly(styrene-co-methyl methacrylate) [poly(AAm-co-AAc)-g-poly(St-co-MMA)] The chemical structure of poly(AAm-co-AAc)-g-poly(St-co-MMA) microgels was proposed. The effect of MBA contents on the degree of cross-linking (%), water absorbency (EWC, %), glass transition temperature, Tg and thermal degradation were studied. The degree of cross-linking (%) and EWC, % increased at 1.5 to 1.675 wt.% of MBA might be due to mono cross-links of MBA. The fluctuation of Tg and melting temperature (Tm) from 1.85 to 2.2 wt.% of MBA might be due to di, poly and cyclic cross-links of MBA. Decomposition of poly(AAm-co-AAc)-g-poly(St-co-MMA) was slightly affected by increasing in MBA contents from 1.5 to 2.2 wt.%. Tg of poly(AAm-co-AAc)-g-poly(St-co-MMA) was decreased at 1.5 to 1.675 wt.% of MBA due to increase in ordered structure and crystallinity content, which led to an increase in Tm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.