Abstract
Mixed maghemite–magnetite has been used as adsorbent for Cr(VI) removal in this study. Results show that the adsorption capacity is enhanced with an increase in reaction temperature and decrease in free energy change. Thermodynamic study shows that Cr(VI) adsorption on the mixed maghemite and magnetite is endothermic in nature and is dependent on solution pH between 3 and 6. X-ray photoelectron spectroscopy (XPS) results demonstrate the theoretical multiplet peaks for iron and chromium adsorbed iron at the surface of the γ-Fe2O3 and Fe3O4 mixture. Theoretical multiplet analysis shows that during Cr adsorption, the amount of maghemite increases (from 70 to 89%). In magnetite spectra, the relative content of Fe(II) decreases from 8.2 to 3.6% indicating the reduction of magnetite in the mixture particles. In Raman spectroscopy studies, clear peaks of chromium on iron oxide were generated at 826cm−1, which could be attributed to chemical interactions between chromium compound and iron oxide. From the results of Raman and XPS studies, electrostatic attraction and oxidation–reduction between chromium and mixed maghemite–magnetite are postulated as mechanisms for the removal of Cr(VI) from aqueous solutions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.