Abstract
ABSTRACTWe have studied the chemical stability of reactively sputtered aluminum nitride film with plasma-enhanced chemical vapor deposited SiO2 and SiNx films. It was found that the PECVD SiO2 film reacted with A1N to form aluminosilicate (3Al2O3·2SiO2) at the SiO2/A1N interface after annealing above 550°C. The presence of Al-0 bonds at the SiO2/AlN interface was verified with x-ray photoelectron spectroscopy and x-ray induced Auger electron spectroscopy. The formation of aluminosilicate resulted in significant decrease in the wet etch rate of A1N layer. For SiNx/AlN/Si layered structure, no interfacial reactions were detected at the SiNx/AlN interface after annealing up to 850°C. These results confirm the thermodynamic predictions on the mutual stability of SiNx/AlN and SiO2/AlN.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.