Abstract
The effect of solid state heat treatment at 913 K on extruded XD Al/TiC metal matrix composite with 0.7 and 4.0 μm particle sizes has been investigated. The interfaces between Al and TiC after extrusion were atomically abrupt, as observed by HRTEM. On holding at 913 K, the composite with submicron particle size showed substantial changes in the phases present due to reaction between Al and TiC at 913 K. The stable reaction products are Al3Ti and Al4C3. A substantial increase in Young's modulus occurs. The room and elevated temperature strength and hardness of the composite with submicron particles also increase significantly with time of heat treatment, but at the expense of ductility. The effect of heat treatment over the time range investigated is limited to the interfaces for the 4.0 μm TiC particle size composite due to longer diffusion paths.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.