Abstract
The chemical order of three off-stoichiometry Ni–Mn–Ga compositions has been measured in the austenitic phase using powder and single-crystal neutron diffraction. The compositions studied, 48–52 at.% nickel, having excess manganese and deficient in gallium, are of technical interest due to the observed large room-temperature, magnetic-field-induced strain. It has been determined that compositions with less than 50% nickel have the excess Mn atoms occupying Ni and Ga sites. Compositions enriched in nickel are best fit with Ni atoms in excess of 50% occupying Mn sites while the excess and displaced Mn occupy Ga sites. The saturation magnetic moments calculated from the site occupations determined here and using Ni and Mn moments reported for Ni2MnGa, agree within 4% with the low-temperature measured moments.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.