Abstract
Long-term stability and durability of gaskets in Proton Exchange Membrane (PEM) fuel cell are important to both sealing and the electrochemical performance of PEM fuel cells. In this paper, the time-dependent aging process of silicone rubber, which is one of the potential gasket materials for PEM fuel cells, is investigated in one simulated PEM fuel cell environment and three accelerated durability test (ADT) media at 70 °C. Optical microscopy is employed to observe the topographical changes on the surfaces of samples. Attenuated total reflection Fourier transform infrared (ATR-FTIR) spectroscopy and X-ray photoelectron spectroscopy (XPS) are used to study the surface chemistry of the samples before and after exposure to the test environments over time. The optical microscopy results indicate that the surface conditions of the samples change from initially smooth to rough, crack appearance and finally crack propagation. The ATR-FTIR and XPS results reveal that the degradation mechanisms of the silicone rubber are likely due to the de-crosslinking and chain scission in the backbone, and the acid has a significant effect on the degradation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.