Abstract
The demonstration of the charge-to-spin conversion, especially with enhanced spin Hall conductivity, is crucial for the development of energy-efficient spintronic devices such as spin–orbit torque (SOT) based magnetoresistive random access memories. In this work, fully epitaxial Ru/Cu heterostructures were fabricated with interface engineering and nanolayer insertions consisting of Cu (1 nm)/Ru (1 nm) structures with different numbers of periods. The atomically controlled interface was confirmed by the high-resolution high-angle annular dark-field scanning transmission electron microscopy, and the epitaxial relationship persists even in the hybrid nanolayer insertion structures. The spin current generation was detected by the measurement of unidirectional spin Hall magnetoresistance, and the effective damping-like spin Hall efficiency (ξ DL) was further quantitatively evaluated by the spin-torque ferromagnetic resonance with thickness dependence of the ferromagnetic layer. It is found that the sharp interface Ru/Cu film has a sizeable ξ DL of −2.2% and the insertion of Cu/Ru nanolayers at the interface can increase the ξ DL value to −3.7%. The former could be attributed to the interface spin–orbit filtering effect and the latter may be further understood by the intrinsic contribution from the local electronic structure tuning due to the lattice distortion near the interface. A large effective spin Hall conductivity is achieved to be (3∼5) × 105 Ω−1 m−1 in the epitaxial Ru/Cu hybrid nanolayers, which is in the same range as that of platinum. This work indicates that the interfacial control with hybrid nanolayer structures can extend the SOT-based materials to highly conductive metals, even with weak spin–orbit interactions, toward high stability, low cost, and low energy consumption for spintronic applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.