Abstract
Before using basic oxygen furnace slag (BOFS) in any engineering application, it is important to determine its properties. The chemical composition, mineralogy, and physical properties of BOF slag are subject to large fluctuations as a result of different raw additives, different compositions of the molten iron used for producing the steel, oxygen stirring of a molten pool, uneven temperature fields, and other complex physical conditions. Thus, in this research, the engineering properties of BOF slag aggregates with different ages were identified, and then the feasibility of BOF slag aggregates in mortar application was investigated. It was found that stockpiled BOFS was harder than fresh BOF slag, which had lower aggregate crushing values and lower LA abrasion values. Also, stockpiled BOFS showed less expansion than fresh BOF slag regardless of water and 1 M NaOH solution immersion. The chemical reaction between f-CaO, f-MgO, and water due to weathering in the field extremely reduced the expansion of BOFS submerged in water. BOFS may contain reactive silica, which causes an alkali–silica reaction (ASR). Stockpiled BOFS (100%, 75%, 50%, 25%) used as a mineral filler in asphalt concrete mix brought about low tensile strength at break up (crack), low compressive strength at +50 °C, poor cohesion, and residual porosity. However, these parameters were partially improved with the use of a thermostable adhesive additive for road bitumen based on polyphosphoric acid esters. The comprehensive assessment in this study indicates that while some mixtures meet the specified criteria for certain properties, there are challenges, particularly regarding crack resistance and cohesion, that need to be addressed to fully align with the standard. Adjustments to the mixture proportions, the exploration of alternative additives, and the use of different types of fillers may be necessary to achieve the desired properties, especially in terms of crack resistance and cohesion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.