Abstract
A new type of defects, vacant broken line defects, was found to occur in a-face grown crystals of 4H-Silicon Carbide. We characterized the vacant broken line defects by high voltage transmission electron microscope (HV-TEM). The HV-TEM image revealed that the edges of broken line defects were connected by a bundle of dislocations, which elongated to the growth direction on the basal plane. The analysis by gb method for determining Burgers vector indicated that the dislocations were not pure screw dislocations, but complex of screw and edge dislocations. The vacant broken line defect was considered to be a quasi-stable state of a bundle of basal plane dislocations in a-face growth, similar to a micropipe defect in c-face growth.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.