Abstract
Ultrasonic spot welded (USWed) Mg-to-bare steel, Mg-to-galvanized steel and Mg-to-bare steel with Sn interlayer (placed in-between Mg and bare steel) were studied. Weak joining occurred in the USWed Mg-to-bare steel, since Mg and Fe do not react with each other. The intermetallic compounds (IMCs) of Mg7Zn3 and Mg2Zn11, which led to the failure of the joint, were largely present in the USWed Mg-to-galvanized steel joint. The introduction of a Sn interlayer in the USWed Mg-to-bare steel actively worked as an intermediate medium to join Mg to Fe, and led to the presence of a distinctive composite-like Sn and Mg2Sn eutectic structure. The lap shear strength of Mg-to-bare steel with Sn interlayer joint was significantly higher than that of the Mg-to-bare steel and Mg-to-galvanized steel joints. Failure during the tensile lap shear tests occurred mainly in the partial nugget pull-out mode in the dissimilar joints of Mg-to-bare steel with Sn interlayer. All the joints of Mg-to-galvanized steel failed from the interface (cohesive failure). The addition of Sn interlayer resulted in energy saving since the welding energy required to achieve the maximum strength decreased from 1750 to 1500J in the Mg-to-steel joints.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.