Abstract
Two-phase (B2+L1 2) nickel aluminide intermetallic compounds were synthesized by the pressure-assisted volume combustion synthesis (CS). The production and characterization of the samples containing NiAl+Ni 3Al were investigated. Aluminum (99% pure, 15 μm) and carbonyl nickel (99.8 pure, 4–7 μm) powders were used. The production of intermetallic compound was carried out at 1050 °C under 150 MPa uniaxial pressure in open air atmosphere in an electrical resistance furnace for 60 min. The formation temperature of intermetallic compound was determined by differential scanning calorimeter (DSC) analysis, and exothermic temperature of powder mixture was determined as 653 °C. The characterization of samples was confirmed by optical microscope, SEM and XRD analysis. It was observed that the structure of compound has very low porosity and the formation of NiAl was completed successfully. The relative density of test materials measured according to Archimedes’ principle was 98.04%. The microhardness of test materials was about 351 HVN 1.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.