Abstract
The charge-to-mass ratio (q/m) of individual particles plays a vital role in the powder coating process. Simultaneous measurements of particle size and electrostatic charge were performed on triboelectrically charged powder paint and other powders in the particle size range 1.0 to 65.0 /spl mu/m in diameter. An electrical single particle aerodynamic relaxation time (ESPART) analyzer was used to measure electrostatic charge (q) and aerodynamic size (d/sub a/) distributions on a single particle basis and in a noninvasive manner. The powders were triboelectrically charged against nonconducting surfaces. Experimental data show that (1) the magnitude of the charge increases linearly with the surface area of the particle and consequently, the charge-to-mass ratio of the particles decreases inversely with respect to d/sub a/ in the entire size range, and (2) twenty to sixty percent of the particles were charged with opposite polarity. The average charge attained by particles larger than 4.0 /spl mu/m in diameter was less than the Gaussian limit of saturation charge. The charge-to-mass ratio of the bulk powder sample depends upon the range of particle size in the sample. The mass median aerodynamic diameter of the sample studied was 30.0 /spl mu/m with the geometric standard deviation of 2.0. >
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.