Characterization of thin film tandem solar cells by radiofrequency pulsed glow discharge – Time of flight mass spectrometry

Abstract

Beside low production costs and the use of nontoxic and abundant raw materials, silicon based thin-film solar cells have the advantage to be built up as multi junction devices like tandem or triple junction solar cells. Silicon thin film modules made of tandem cells with hydrogenated amorphous silicon (a-Si:H) top cell and microcrystalline (μc) Si:H bottom cell are available on the market. In this work, the analytical potential of state-of-the art radiofrequency (rf) pulsed glow discharge (PGD) time of flight mass spectrometry (TOFMS) commercial instrumentation is investigated for depth profiling analysis of tandem-junctions solar cells on 2mm thick glass substrate with 1µm thick ZnO:Al. Depth profile characterization of two thin film tandem photovoltaic devices was compared using millisecond and sub-millisecond rf-PGD regimes, as well as the so-called “low mass mode” available in the commercial instrument used. Two procedures for sample preparation, namely using flat or rough cell substrates, were compared and the distribution of dopant elements (phosphorous, boron and germanium) was investigated in both cases. Experimental results obtained by rf-PGD-TOFMS as well as electrical measurements of the samples showed that a worse depth resolution of dopant elements in the silicon layers (e.g. distribution of boron in a thicker region that suggests a diffusion of this dopant in the coating of the sample) found using a rough sample substrate was related to a higher power conversion efficiency.