Abstract
This paper presents preliminary results concerning Al 2O 3–Ni composites fabricated by sintering under a high pressure of 7.7 GPa, at a temperature below the melting temperature of nickel. The microstructure of composites was characterized by scanning and transmission electron microscopy. Quantitative measurements of size, shape and distribution of metal particles were based on image analysis. A correlation between the size of the Ni particles and their location has been found. Small Ni particles, with a grain size in the range of 50–500 nm, are mostly located inside the ceramic grains. Some Ni particles are also situated at the grain boundaries, and large particles are surrounded by ceramic grains. The shape of the ceramic grains suggests that the ceramic powder particles underwent deformation during the process of consolidation under high pressure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.