Mechanical properties of extruded WZ72 magnesium alloy with long-period stacking ordered (LPSO) phase were investigated during compression loading at room temperature and at a constant strain rate of 10-3 s-1. The samples of (8 x 4 x 4) mm3 were compressed along three directions with respect to the lamellar LPSO-phase: parallel (ED), perpendicular (TD) and under 45°. Concurrently with the deformation tests, the acoustic emission (AE) response of the specimens was recorded. The AE measurements revealed that both the twinning activity and the kinking of the LPSO phase significantly depend on the orientation of LPSO phase. The highest strength was observed for the sample which was compressed parallel to the LPSO phase (extrusion direction). The highest AE activity was also measured in this sample.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.