Abstract
Development of reversible solid oxide cells (RSOCs) must face one major challenge of the poor reliability origination from the oxidization of Ni-based hydrogen electrode materials. In this work, Sr2Fe1.5Mo0.5O6-δ -Gd0.1Ce0.9O1.95 (SFM-GDC) symmetrical electrode working both air and hydrogen electrode is designed and investigated for RSOCs. Regardless of the redox condition, SFM shows excellent structural stability by the XRD analysis and HR-TEM observation. Meanwhile, XPS analysis obviously demonstrates the co-existence of Fe2+/Fe3+ and Mo5+/Mo6+ couples, of which both proportions increase with the reduce oxygen partial pressure. Applying SFM-GDC symmetrical electrode, the 300 μm-thick YSZ electrolyte-supported RSOCs with GDC buffer layers show acceptance electrochemical performance, and switch smoothly between power generation and electrolysis modes with no obvious degradation after 20 h short-term stability working under humidified (∼3%H2O) H2 and 3%H2O-air atmospheres, respectively. Besides, the impedance spectrum were further studied using a relaxation time distribution function (DRT), and two polarization peaks (P1, P2) observed in the power generation mode shifted to the left at low frequency with the reduced temperature, while one more new polarization peak (P3) corresponds to the reaction gas diffusion owing to the low concentration steam (∼3% H2O) in electrolysis mode. This research highlights that the stable and efficient SFM-GDC symmetrical electrode can be the potential RSOCs electrode candidates.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have