Abstract
Çan, Çatalağzı, Seyitömer and Afşin-Elbistan thermal power plant fly ashes were used to investigate the sintering behavior of fly ashes. For this purpose, coal fly ash samples were sintered to form ceramic materials without the addition of any inorganic additives or organic binders. In sample preparation, 1.5 g of fly ash was mixed in a mortar with water. Fly ash samples were uniaxially pressed at 40 MPa to achieve a reasonable strength. The powder compacts were sintered in air. X-ray diffraction analysis revealed that quartz (SiO 2), mullite (Al 6Si 2O 13), anorthite (CaAl 2Si 2O 8), gehlenite (Ca 2Al 2SiO 7) and wollastonite (CaSiO 3) phases occurred in the sintered samples. Scanning electron microscopy investigations were conducted on the sintered coal fly ash samples to investigate the microstructural evolution of the samples. Different crystalline structures were observed in the sintered samples. The sintered samples were obtained having high density, low water adsorption and porosity values. Higher Al 2O 3 + SiO 2 contents caused to better properties in the sintered materials.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.