Abstract
We have found undiscovered defects on a 4H-SiC epitaxial layer, the shape of which resembles a scraper in images taken by confocal differential interference contrast optical microscopy. The surface morphological structure and formation mechanism of the scraper-shaped defects were investigated by atomic force microscopy and grazing incidence monochromatic synchrotron X-ray topography, respectively. The scraper-shaped defects were surface morphological defects consisting of surface asperity and were caused by the migration of interfacial dislocations. The evaluation of the thermal oxide reliability of metal–oxide–semiconductor capacitors fabricated on these defects was performed by time-dependent dielectric breakdown measurement. The degradation of thermal oxide occurred only on the downstream line of the scraper-shaped defects. The thickness of the oxide layer on these defects was also investigated using cross-sectional transmission electron microscopy.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.