Abstract
Porous NiTi alloys are highly attractive for energy absorbers, damping devices and biomedical implants. In the present work, metal injection moulding (MIM) in combination with the application of a suitable space holder material was used for the production of NiTi parts with well defined pore sizes and porosities in the range of 30–70vol.%. For comparing the properties, porous titanium and Ti–6Al–4V samples were prepared in the same manner.Focus of the present work was a detailed investigation of the mechanical properties of porous NiTi to estimate its potential regarding the abovementioned applications. For a Ni-rich NiTi alloy with a porosity of 50vol.%, fully pronounced pseudoelasticity after 6% compression was demonstrated. An energy dissipation of 1.5MJ/m3 was measured, which could be directly related to the reversible austenite–martensite phase transformation. At higher deformations, pseudoelasticity becomes more and more superposed by the onset of plastic deformation. Nevertheless, even at deformations of up to 50%, a clearly pronounced amount of pseudoelastic shape recovery still remained. Fatigue of pseudoelasticity was investigated by conducting of up to 230,000 load cycles to 4% compression at a frequency of 1Hz.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.