Abstract
The surfaces of virgin and chemically etched poly(tetrafluoroethylene) (PTFE) have been studied using atomic force microscopy (AFM) in both contact and tapping modes. While attempting to perform AFM in contact mode on this relatively soft polymeric material, tip-induced imaging artifacts (presumably due to blunt tips and tip-to-surface interactions) were identified when the results were compared to scanning electron microscopy (SEM) surface images. When subsequent AFM imaging was performed in tapping mode it was apparent that these tip-induced artifacts were eliminated. Comparable tapping mode AFM and SEM images were obtained for even the highly porous, unstable surface that results from sodium naphthalenide etching of PTFE. AFM imaging in tapping mode of virgin and etched PTFE surfaces shows the three-dimensional character of the etched surface necessary for mechanical interlocking and resultant strong adhesion.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.