Abstract
Energy-filtering transmission electron microscopy (EFTEM) was applied for investigating interfaces between a polymer and an adhesive. The sample employed in this work is polybutylene terephtharate (PBT) sheets laminated with an epoxy adhesive. It was found that heat aging of the PBT at 180 degrees C in air for > 9 h prior to adhesion decreases the adhesion strength drastically. To investigate this unfavourable aging effect on the adhesion strength, we performed elemental mapping and image EELS using EFTEM. A weak boundary layer with a thickness of < 50 nm was visualized at the PBT-adhesive interface by elemental mapping in the sample subjected to the heat aging and image EELS revealed the origin of this layer. Thus, we clearly correlated the nanoscale interfacial structure with the adhesion strength by EFTEM.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.