Abstract
ABSTRACTOxide dispersion strengthened austenitic stainless steel (ODS316), which is based on advanced SUS316 steel, has been developed by mechanically alloying and hot extrusion. Hafnium and titanium were added to make a fine distribution of oxide particles. The stability of oxide particles dispersed in ODS316 under irradiation was evaluated after 250 keV Fe+ irradiation up to high doses at 500 °C. TEM observation and EDS analysis indicated that fine complex oxide particles with Y, Hf and Ti were mainly dispersed in the matrix. There are no significant changes in the distribution and the size of oxide particles after irradiation. It was also revealed that the constitution ratio of Ti in complex oxide appeared to be decreased after irradiation. This diffuse-out of Ti during irradiation could be explained by the difference in oxide formation energy among alloying elements.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.