Abstract
The citric-acid coated Mn-Zn ferrite nanocrystalline was prepared by an improved co-precipitation method. X-ray diffraction (XRD) and TEM measurements indicated that the coated samples were pure spinel Mn-Zn ferrite nanocrystalline and the particles coated after boiling circumfluence were more homogeneous than that before boiling circumfluence. Vibrating sample magnetometer (VSM) indicated that the Ms of the coated samples was higher than that without coating. Specially when the content of citric acid is 4.76wt% after boiling circumfluence, the Ms of the coated sample is 54.15 emu•g-1 which is 28.7% higher than that without coating.