Abstract
Nano-particle Co1−x Zn x Fe2O4 (x = 0.0, 0.3, 0.5, 0.7, and 1.0) samples were prepared via combustion route using Alove Vera Gel. XRD, IR, and SAED analysis represents single-phase formation of ferrite samples, and nano-sizes of the particles in the range of 6 to 13 nm were confirmed using XRD data and TEM images. Decrease in lattice constant with increasing Zn content reflects formation of compositionally homogeneous samples. Dielectric constant and dielectric loss study showed promising results. The room temperature Mossbauer spectrum showed mixed superparamagnetic and ordered ferromagnetic behavior. The possible modification in the cation distributions was seen in the nano-particle ZnFe2O4 sample obtained in the present work compared to conventional bulk samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.