Abstract
In the present work, we report a Cu-Mn alloy as a material for the self-forming barrier process, and we investigated the diffusion barrier properties of the self-formed layer on low-k dielectrics with or without UV curing treatment. Cu alloy films with 3.8 at% Mn were directly deposited onto low-k dielectrics by co-sputtering followed by annealing at various temperatures. The self-formed layers were investigated by transmission electron microscopy (TEM) and energy-dispersive X-ray spectroscopy (EDS). In order to compare barrier properties between the Mn-based self-formed layer on low-k dielectric with UV curing and the interlayer on low-k dielectric without UV curing, thermal stability was measured at various thermal stress temperatures. Our results indicated that the formation of the barrier at the interface of Cu-Mn alloy/low-k dielectric was enhanced by UV curing due to changes in the porosity and C concentration in the dielectric layer.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.