Abstract
Micro computed tomography (Micro-CT) was applied to obtain three-dimensional images of the microstructure of cement paste (water-to-cement mass ratio of 0.5) at different ages. By using the Amira software, component phases of the cement paste such as pores, hydration products, and unhydrated clinker particles were segmented from each other based on their 3D image grey levels; their relative contents were also calculated with the software, and the data are 61.2%, 0% and 38.8% at the beginning of hydration and 11.8%, 78.5% and 9.7% at 28 d age, respectively. The hydration degree of cement paste at different ages was compared with the experimental data acquired by loss on ignition (LOI) tests. The results show that the calculated and measured data reasonably agree with each other, which indicates that micro-CT is a useful and reliable approach to characterize the micro structure evolution of hydrating cement paste.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.