Characterization of magnetic and dielectric properties of Bi(1-x)Gd(x)FeO3 nanoparticles by local structure analyses.

Abstract

Bi(1-x)Gd(x)FeO3 (0 < or = x < or = 1.0) nanoparticles were synthesized by a wet chemical method. The annealing temperatures were controlled to obtain single-phase Bi(1-x)Gd(x)FeO3 nanoparticles. The crystal diameters decreased as the number of doped Gd ions increased. The crystal structure changed, as the number of Gd ions increased, from rhombohedral to orthorhombic perovskite, at x = 0.2. The behavior of the magnetization curves observed at various values of x (x = 0.05, 0.1, 0.15) of the rhombohedral structure suggested that the canted antiferromagnetism and remanent magnetization (M(r)) drastically increased, compared with those at x = 0 (BiFeO3). It is suggested that the spin-canting angle of the Fe ions increased with the increase in the number of Gd ions. The dielectric properties at x = 0.1 showed that the dielectric loss (tan delta) was improved, compared with that at x = 0 (BiFeO3), by approximately 90%, while the real part of the dielectric constant epsilon' was reduced by approximately 15%. The reason is that the doping impurities restrained the reduction in the leakage current. It was found, from the X-ray absorption fine structure (XAFS) spectra, that Gd ions were doped accurately and that the symmetry of the B site was improved. The Mössbauer analysis suggested the existence of magnetic cycloid spiral ordering.