Abstract
Layered polysilane synthesized according to a new recipe was characterized mainly by photoluminescence (PL) measurement. The PL spectrum of the as-prepared sample had a broad peak at 2.0 eV. The PL peak of a sample annealed at 300°C was also at 2.0 eV, and its PL intensity was several times greater than that of the as-prepared sample. The PL peak of a sample annealed at 400°C was red-shifted and its PL intensity was lower than those of the others. On the other hand, the PL emission from a sample rinsed in HF solution was blue-shifted and had a little lower intensity. The interpretations of the experimental results are discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.