Abstract
In the design of hot forming processes for aluminum alloys, hot processing maps are usually used as a powerful tool for processing parameters optimizations. Although the stability of deformation is considered in conventional hot processing (CHP) maps, the difficulty of deformation, i.e., whether deformation is easy to occur, is not taken into account. Therefore, it is difficult for CHP maps to efficiently and accurately obtain the optimal processing parameters and achieve satisfying hot workability. Hence, in this study, thermal compression tests were performed to investigate the hot forming behavior of 5052 aluminum alloy in the deformation temperature range of 553-733 K and strain rate range of 0.001-1 s−1. We proposed an activation energy-processing (AEP) map by coupling the CHP map and the activation energy value, and thereby applied it to evaluate the hot workability of 5052 aluminum alloy. In CHP maps, the region with the highest power dissipation efficiency is generally considered to be the best processing region. However, the AEP map shows that materials with satisfying hot workability not only depends on high power dissipation efficiency, but also on low activation energy values. At the strain of 0.7, the optimal hot processing region predicted by the CHP map lies in the temperature range of 583-673 K and strain rate range of 0.001-0.1 s−1, but that predicted by AEP map locates in the temperature range of 643-733 K and strain rate range of 0.001-0.1 s−1. Microstructure characterization implies that the optimal processing region predicted by the CHP map presents necklace-like structures, which are non-uniform and unbeneficial for deformation, while that predicted by the AEP map consists of fine, uniform and equiaxed grains. Thus, it is implied that the processing regions predicted by the AEP map are more suitable for forming, i.e., the reasonability of the AEP map is verified.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.