Abstract
To obtain the optimal mechanical properties, several processes including spray forming technology, two passes hot extrusion and substantial heating treatments were operated on an Al-Zn-Mg-Cu-Zr alloy. The characterization methods used in this study include tensile tests, X-ray diffraction, differential scanning calorimetry and microstructure observations by optical microscope, scanning and transmission electron microscopy. The typical characteristics were the refined grain, homogeneous precipitates and porosity in the as-deposited pre-forms. The ultimate tensile strength, yield strength, hardness and elongation improved significantly after two passes hot extrusion. A good combination of ultimate tensile strength at 704 MPa and elongation at 9.7% were achieved under peak-aged treatment. The best ultimate tensile strength was obtained at 732 MPa after re-aging and regression. It was main dimple fracture in the extruded and aging treated specimens while brittle fracture for the as-deposited. The secondary phases were main MgZn2 and Al3Zr dispersoids throughout all the states. The contributions of grain boundaries, dislocations, solid-solution and precipitates on the yield strength were analyzed using a quantitative equation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.