Characterization of high thermal conductivity fuel surrogates before and after ion irradiation

Abstract

• Thermal conductivity of UO 2 surrogates was enhanced during sintering using aluminum oxide and silicon carbide additives. • Compositions were stable up to 5 dpa and 700 °C while a decrease in their mechanical properties was observed at 15 dpa. • Microcrack formation due to anisotropic swelling of the additives was not observed. High thermal conductivity nuclear fuels offer important potential advantages over traditional oxide-based fuels such as higher burnup, reduction in fission gas release, and better overall safety of the system. One proposed approach to high thermal conductivity fuels utilizes high thermal conductivity nonfissile additives with UO 2 fuel to lower the fuel operating temperature and thereby take advantage of the highly favorable radiation resistance of UO 2 at lower operating temperatures. However, differential swelling in the matrix and high conductivity additive phases during high dose irradiation could lead to internal cracking and poor performance. In the current study, ceria (CeO 2 ) and zirconia (ZrO 2 ) surrogate matrices were used to model UO 2 behavior. Additives of 10 vol. % Al 2 O 3 or SiC in the form of short fibers or platelets were used for the high conductivity second phase. The nuclear fuel surrogates were sintered to achieve densities greater than 93% of the ideal values. Scanning electron microscopy (SEM) imaging and X-ray diffraction confirmed the uniform distribution of the second phase and that no intermetallic second phase was formed during sintering. The thermal conductivity of the sintered samples was measured from 50 °C to 900 °C and confirmed the desirable increase compared to pure CeO 2 /ZrO 2 pellets. Samples were irradiated with 20 MeV Ni 6+ ions at midrange doses ranging from 1 to 15 displacements per atom (dpa) and temperatures from 300 °C to 700 °C. Post irradiation characterization revealed a good stability of the samples at low to medium doses with matrix lattice parameter swelling of < 0.14 % but showed a significant microstructural deterioration and decrease of the mechanical properties at 15 dpa.