Abstract
ABSTRACT The fibre of Grewia bicolor bark (GB) was extracted and used as reinforcement for the development fibreboards using orthophtalique unsaturated polyester (UP) as a matrix. Two methods of extraction of fibres were used, namely biological retting and chemical extraction by a sodium hydroxide solution at a 5% concentration. Chemical, Physical, mechanical, and thermal characteristics were determined using ATF FTIR, mechanical test and thermogravimetric analysis. The theoretical density of the characterized fibres was 1.30 g/cm3. The porosity decreases by 5% from the root to the leaves. The SEM analysis indicated the presence of fibrils coated with a rough sheath similar to a honeycomb cell structure. The use of NaOH in the extraction method removes the hemicellulose, pectin, wax, and lignin from the fibres. The average elasticity modulus of untreated and treated fibres are, respectively, E = 35.18 ± 2.25 MPa and E = 33.47 ± 2.35 MPa and internal bond of fibreboards are 0.98 ± 0.05 MPa and 1.06 ± 0.02 MPa.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.