Characterization of flow-through micropores in MFI membranes by permporometry

Abstract

Abstract Permporometry was used for the first time to characterize flow-through micropore defects down to 0.7 nm in size in MFI zeolite membranes. Helium was used as the non-adsorbing gas and n-hexane or benzene was used as the adsorbate. The helium flow through zeolite pores was estimated using percolation theory and the remaining flow was assigned to flow-through defects. The area distribution of flow-through defects was estimated from the data using a simple model and similar results were obtained using both adsorbates. The total area of defects determined using n-hexane as the adsorbate was as low as about 0.7% of the membrane area and defects with a width below 1 nm constituted 97% of the total defect area for the best membrane. The permporometry results were supported by n-hexane/1,3,5-trimethylbenzene separation experiments. The permporometry data were also consistent with HR-SEM observations indicating the presence of narrow open grain boundaries, and absence of large cracks and pinholes.