Abstract
In the past decade, aluminum scandium nitride (AlScN) with a high Sc content has shown ferroelectric properties, which provides a new option for CMOS-process-compatible ferroelectric memory, sensors and actuators, as well as tunable devices. In this paper, the ferroelectric properties of grown on different metals were studied. The effect of metal and abnormal orientation grains (AOGs) on ferroelectric properties was observed. A coercive field of approximately 3 MV/cm and a large remanent polarization of more than 100 μC/cm2 were exhibited on the Pt surface. The thin film grown on the Mo metal surface exhibited a large leakage current. We analyzed the leakage current of during polarization with the polarization frequency, and found that the films grown on either Pt or Mo surfaces have large leakage currents at frequencies below 5 kHz. The leakage current decreases significantly as the frequency approaches 10 kHz. The positive up negative down (PUND) measurement was used to obtain the remanent polarization of the films, and it was found that the remanent polarization values were not the same in the positive and negative directions, indicating that the electrode material has an effect on the ferroelectric properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.