Abstract
Epitaxially grown YBa/sub 2/Cu/sub 3/O/sub 7-/spl delta// (Y-123) thin films have been successfully deposited on single crystal SrTiO/sub 3/ substrates by a pulsed ion-beam evaporation (IBE) method. A cation-stoichiometric Y-123 target was bombarded by protons with an energy of 1 MeV (peak) using a pulsed ion beam generator ('ETIGO-II'). The ablation plasma was deposited on SrTiO/sub 3/ single crystal substrates. The thin films were heat-treated at 900/spl deg/C for 2 h and 650/spl deg/C for 5 h in flowing oxygen gas. The X-ray diffraction (XRD) pattern for an annealed thin film revealed that a single-phase, c-axis-oriented Y-123 thin film was obtained. Since a fourfold symmetry was observed in a [102] pole figure, the Y-123 thin film was concluded to be epitaxially grown on the SrTiO/sub 3/ substrate. From high-speed photographs of the time evolution of the plasma, the instantaneous deposition rate of the film was estimated to be approximately 5 mm/s.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.