Abstract
Cu(In,Ga)3Se5 films were deposited on soda-lime glass substrate by three-stage co-evaporation process. In the film, the band gap increased as the Cu content decreased and also as the Ga content increased. The grain size became smaller as the Ga content increased. In the Cu1.29(In1-xGax)3Se5 system, the maximum hole concentration was 1x1015 /cm3 when the Ga content was 0.5 and its band gap was 1.45 eV. Comparing the conventional CIGS solar cell with Cu0.8(In0.7Ga0.3)Se2 film, the series resistance is too large, indicating that further p-type doping in the Cu(In,Ga)3Se5 film is necessary to improve cell efficiency for the top cell application in CIGS tandem solar cells.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.