Abstract
Diamond-like carbon (DLC) films have been extensively studied for more than a decade due to their unique combination of properties. The internal compressive stress affects their adhesion and preventing wide usage of these films. Metal-containing DLC films are expected to relax internal stress. The present work focused on the synthesis, chemical bond and mechanical property characterization of Cr-containing DLC films. The films thickness, internal stress and composition were characterized by scanning electron microscopy, optical interferometry and X-ray photoelectron spectroscopy respectively. Incorporation of Cr into DLC causes an initial internal stress reduction and subsequent stabilization around 0.5 GPa. The hardness behavior was found to depend on Cr content. Films with less than 7.36 at.% Cr (no formation of C-Cr bond) showed a dramatically hardness reduction compared to pure DLC films. Above 7.36 at.% Cr (C-Cr bond formed) the hardness increases above 12 GPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.