Abstract
β- TCP was synthesized by changing the process parameters and all samples were characterized in terms of density, porosity, XRD and FTIR analysis. Density rose and porosity decreased with rising of pH value and density found maximum (2.31 g/cc) at pH 10. Sharp peaks in the XRD diffractograms ensured the crystallinity of samples which increased after calcination and sintering process. Average crystal size was found 28.21 nm. IR spectrum at 943.19 cm-1 and 972.12 cm-1 appeared in FTIR analysis proved the presence of pure β- TCP exists in resulting samples. Performance to stress increased with pH and maximum compressive strength was found at pH 10. Calcination was found maximum 3.485 Nmm-2 at 900°C minimum 1.352 Nmm-2 at 800°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Bioengineering & Biomedical Science
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.