Abstract
Abstract Al-doped ZnO (AZO) film was deposited by direct-current (DC) magnetron sputtering on p-Si (1 0 0) wafer to fabricate Al-doped n-ZnO/p-Si heterojunctions. The microstructural, optical and electrical properties of the AZO film were characterized by XRD, SEM; UV–vis spectrophotometer; four-point probe and Hall effect measurement, respectively. Results show that the AZO film is of good quality. The electrical junction properties were investigated by I–V measurement, which reveals that the heterojunction shows rectifying behavior under a dark condition. The ideality factor and the saturation current of this diode are 20.1 and 1.19×10 −4 A, respectively. The value of I F / I R ( I F and I R stand for forward and reverse current, respectively) at 5 V is found to be as high as 19.7. It shows fairly good rectifying behavior, indicating formation of a diode between AZO and p-Si. High photocurrent is obtained under a reverse bias when the crystalline quality of AZO film is good enough to transmit light into p-Si.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.