Abstract
Amorphous Cr–C alloy coatings were electrodeposited from a trivalent chromium bath containing formic acid. The effects of plating parameters such as pH and current density on composition, structure, morphology and corrosion behaviour of as-deposited coatings were investigated. Results showed that the suitable current density for Cr–C alloy electrodeposition is increased as the pH is decreased. Furthermore, by decreasing the pH, higher amount of carbon was introduced into the coatings. The Cr–C alloy coatings deposited at lower pH showed higher passive current density on Tafel plot. By annealing the amorphous Cr–C alloy coatings at 300 °C, a nanocrystalline structure having higher hardness was obtained. However, the corrosion resistance was seen to be impaired. Annealing at 600 °C led to the precipitation of Cr 23C 6 which resulted in a higher hardness. The formation of Cr 23C 6 enhanced the corrosion resistance of coatings due to an increase in corrosion potential. However, formation of micro-cells between the Cr 23C 6 precipitates and bulk chromium prevented the passive film formation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.