Abstract
Gold catalysts supported on niobia and alumina are active in glycerol oxidation performed in liquid basic solution in the presence of oxygen. Niobia-supported gold is only slightly less active than commercial Au/TiO 2 catalyst. XPS data allow to characterize gold nanoparticles on both supports. IR studies show that CO adsorbs on gold particles loaded on niobia producing well characterized terminal carbonyls whose C–O stretching frequency shifts up by decreasing CO coverage, an usual behaviour for gold carbonyls. Two families of gold nanoparticles on niobia are characterized by CO stretching frequencies of adsorbed CO at 2098–2112 cm −1 after reduction at 573 K and at 2108–2120 and 2125–2135 cm −1 after reduction at 773 K. However, after both reduction pretreatments such gold metal particles coexist with strongly oxidizing gold species which are able to convert CO into CO 2 at 153–193 K. Based on IR and XPS experiments, the lower activity of alumina-supported gold may be due to a lower density of corner and edge sites on Au nanoparticles, associated to the minor dispersing ability of alumina for gold.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.